� Kuraray Liquid Rubber 13
Solvent
L-IR-30, 50
L-IR-410
Solubility of L-IR Hexane, Heptane, Cyclohexane
A
A
Toluene, Xylene
A
A
Methyl Acetate
C
C
Ethyl Acetate
C
A
n-Butyl Acetate
A
A
Acetone
C
C
MEK
C
A
MIPK
B
A
MIBK
A
A
Methanol, Ethanol
C
C
Chloroform
A
A
Polymer content: 20 wt% at 25˚C A: Soluble B: Partially soluble C: Insoluble
Carbon Tetrachloride
A
A
Carbon Disulfide
A
A
Cyclohexanone/Xylene (50/50 wt/wt)
A
A
UV Crosslinking system for UC-102M
100 90 80 70 60 50 40 30 20 10 0
UC-102M/NDDA=50/50 UC-102M/NDDA=75/25 UC-102M/NDDA=100/0
0
5
10
UV irradiation (pass)
Lamp: High pressure mercuray lamp Curing conditions: Light intensity : 40 mW/cm 2 , Conveyor speed : 2 m/ min, 1 Pass = 188 mJ/cm 2 Thickness: 0.8 mm Gel fraction test: Toluene extraction at 25˚C for 24 hours