THERMOSEAL C8200
Typical values refer to 1/16” material unless otherwise specified:
Creep Relaxation ASTM F38B (1/32”)
• Synthetic Fibre
30%
• Hypalon® Binder
Sealability ASTM F37A (1/32”)
< 0.30 ml/hr
• Acid Resistant
Gas Permeability DIN 3535/6
< 0.5 ml/min
• Good Oil-Fuel Resistance
Compressibility ASTM F36J
9%
• Good Gas Sealability
Recovery ASTM F36J
50% minimum
• No Colour Added
Klinger Hot Compression Test
(tested at 3,625-psi gasket stress, and to 392°F
[200°C]) 7% initial 17% additional
Thickness Decrease 73°F (23°C) Thickness Decrease 572°F (300°C)
Weight Increase ASTM F146 after immersion in Fuel B 5h/73°F (23°C) Thickness Increase ASTM F146 after immersion in ASTM Oil 1, 5h/300°F (149°C) ASTM Oil IRM903, 5h/300°F (149°C)
10% maximum
0-5% 5-10% 0-5% 0-10%
ASTM Fuel A, 5h/73°F (23°C) ASTM Fuel B, 5h/73°F (23°C)
Dielectric Strength ASTM D149-95a
9 kV/mm
ASTM F104 Line Call Out
F712100B5E22K6M5
Leachable Chloride Content FSA Method (Typical)
n/a
Density ASTM F1315
106 lb/ft³ (1.7 g/cc)