S9074-AQ-GIB-010/248 Rev 1
1"
DISCARD
1-1/2"
FACE BEND
6" MIN
DISCARD
1-1/2"
ROOT BEND
DISCARD
1"
6" MIN
60° MIN
SEE NOTE 4
T = SEE NOTE 1
1/8" MIN
0" TO 1/8"
NOTES: 1. Performance qualification assembly thickness and thickness range qualified shall be as follows: Test No. Test Assembly Thickness (T) Thickness Range Qualified to Weld 2A Max thickness to be welded in production 1/16 inch to T 2B 3/8 inch 1/16 inch to unlimited 2. Weld should be made with the maximum size welding rod suitable for position of test plate. 3. Joint shall be welded from one side only and joints welded in the vertical position shall be welded upwards. 4. Plate shall not be more than 5 degrees out of parallel after welding. 5. If destructive testing is employed, after VT, weld face reinforcement may be removed as permitted by 5-4.2. Undercutting shall not be removed. No repair welding from the root side shall be permitted. Removal of root side reinforcement of one-sided welds with no backing is not permitted for root bends. 6. Two guided-bend test specimens shall be removed from the test plate if NDT is not employed.
Figure 7-12. Performance Qualification Test Nos. 2A and 2B for Fuel Gas Welding (Plate)
Figure 12. Performance Qualification Test Nos. 2A and 2B for Fuel Gas Welding (Plate).
7-87
Made with FlippingBook - Share PDF online