S9074-AQ-GIB-010/248 Rev 1
10" APPROX.
1/4"
EDGE OF JOINT
1/4"
T
W
2"R
1/4"
THIS SECTION MACHINED, PREFERABLY BY MILLING
W =1-1/2"±0.01 IF "T" DOES NOT EXCEED 1" W =1"±0.01 IF "T" EXCEEDS 1"
REDUCED-SECTION TENSION SPECIMEN (PLATE) FOR BRAZED BUTT & SCARF JOINTS IN PLATE
12-1/2"
1/4"
1/4"
T
X
2"R
T
THIS SECTION MACHINED, PREFERABLY BY MILLING
T MIN
X
T
X
X
1/16" MIN
T
T
FOR LAP JOINTS
ALTERNATE DESIGNS
X = 4T MIN T = 1/4" MIN
Figure 7-19. Reduced Section Tension Specimen (Plate) for Brazed Lap-Type Joints
12" APPROX.
1-1/2"
T
X
SEC. A
Z
SEC. B
Y
FULCRUM POINT
SUFFICIENT FOR PEELING PURPOSES
LAP JOINT PEEL SPECIMEN
NOTES: 1. Flange Y may be omitted from section B when “peeling” is to be accomplished in a suitable tension machine. 2. Specimen shall be brazed from side marked Z. X = 4T minimum or as required by design Figure 19. Reduced Section Tension Specimen (Plate) for Brazed Lap-Type Joints.
Figure 7-20. Lap Joint Peel Specimen
7-96
Made with FlippingBook - Share PDF online