TeXtreme ® 0/90 Woven Spread Tow Reactive Binder (prepreg) Other weights and widths available upon request. The Reactive Binder reinforcements allow ultra-light weight reinforcements, such as Spread Tow products, to be prepregged with low resin contents. The Reactive Binder is mostly suitable for ultra-low fiber areal weight reinforcements, e.g. sub 100 gsm, where low resin contents are requested. It can also be an enabler for ultra-low resin contents on any reinforcement areal weight. The Reactive Binder has an outlife of 12 months at room temperature so refridgeration is not required for shipment or storage. It enables layups of larger, more time consuming structures that normally are limited by a prepregs outlife. It can be repeatably heated to elevated temperatures (max 80°C) for simpler draping and/or pre-stacking without ageing. The Reactive Binder is an epoxy resin system (bisphenol-A based) with minimum 150°C cure temperature. It can be used as the matrix itself on various TeXtreme ® reinforcements or as a binder using subsequent prepregging process or liquid resin composite manufacturing. The Reactive Binder is suitable for aerospace, industrial, racing and sporting goods applications. It can be supplied on TeXtreme ® narrow UD tapes, wide UD tapes, or 0/90 fabrics.
TEXTREME ® SPREAD TOW WOVEN
Carbon Fiber
Article Description
Fiber name
FAW (gsm)
Reac- tive binder (gsm)
Resin content
Total areal weight (gsm)
Tape width (mm)
Weave pattern
Fabric width (mm)
1192 TeXtreme ® 0/90 HS 80 UTS50S 80
49
38% 129 20
PW
1000
HS
1160 TeXtreme ® 0/90 HS 100 TR50 100
61
38% 161 20
PW
1000
1187 TeXtreme ® 0/90 IM 42
MR70 42
26
38% 68
20
PW
1000
IM
1193 TeXtreme ® 0/90 IM 82 IMS65
82
50
38% 132 20
PW
1000
HM 1194 TeXtreme ® 0/90 HM 43 HS40 43
26
38% 69
20
PW
1000
Reactive binder fabrics are suitable for F1 racing cars