Turning Grooving
Cutting Data Recommandation Table
Cutting parameter recommended table of parting off and grooving application AW100K f（mm/rev） f（mm/rev） f（mm/rev） f（mm/rev） f（mm/rev） 0.1 0.3 0.5 0.1 0.3 0.5 0.1 0.3 0.5 0.1 0.3 0.5 0.1 0.2 0.4 AP301U AP130S AP330M AC230P
Materials
Brinell hardness (HB/HRC)
Tensile strength (N/mm 2 )
ISO
Workpiece material
C≤0.25%
Annealed 125
428 180 145 130 180 145 130 160 130 100 220 180 160 - - -
0.25 ＜ C ≤0.55% Annealed 190
639 145 130 115 145 130 115 120 100 90 160 130 115 - - -
0.25 ＜ C ≤0.55% Heat-treated
210
708 130 115 100 130 115 100 120 100 90 130 115 100 - - -
Unalloyed steel
C ＞0.55%
Annealed 190
639 145 130 115 145 130 115 145 130 80 160 130 115 - - -
C ＞0.55%
Heat-treated
300
1013 115 100 80 115 100 80 115 100 80 115 100 80 - - -
Free cutting steel (short-chip) Annealed 220
745 130 115 100 130 115 100 130 115 100 130 115 100 - - -
Annealed
175
591 180145130180145130 - - - - - - - - -
Heat-treated
300
1013 115100 80 115100 80 - - - - - - - - -
Low-alloyed steel
Heat-treated
380
1282 1709010517090105 - - - - - - - - -
Heat-treated
430
1477 ---------------
Annealed
200
675
---------------
High-alloyed steel and high- alloyed tool steel
Hardened and tempered
300
1013 ---------------
Hardened and tempered
400
1361 ---------------
Ferritic/martensitic, annealed
200
675 165135105165135105 - - - - - - - - -
Stainless steel
Martensitic, heat-treated
330
1114 150115 70 150115 70 - - - - - - - - -
Austenitic, quench hardened Austenitic, precipitation hardened (PH) Austenitic/ferritic, duplex
200
675 165 135 105 165 135 105 165 135 105 - - - - - -
Stainless steel
300
1013 155 120 80 155 120 80 155 120 80 - - - - - -
230
778 135 110 85 135 110 85 135 110 85 - - - - - -
Ferritic
200
400 1159065 - - - - - -1159065 - - -
Malleable cast iron
Pearlitic
260
700 1159065 - - - - - -1159065 - - -
Low tensile strength
180
200 185140 95 - - - - - - 200160120 - - -
Grey cast iron
High tensile strength/austenitic
245
350 185140 95 - - - - - - 200160120 - - -
Ferritic
155
400 145110 80 - - - - - - 160130100 - - -
Nodular cast iron
Pearlitic
265
700 145110 80 - - - - - - 160130100 - - -
GGV(CGI)
230
400
---------------
Wrought aluminium alloys Cast aluminium alloys
Non-aging
30
-
---------------
Aged
100
340
---------------
≤ 12% Si, non-aging
75
260
------------850500200
≤ 12% Si, aged
90
310
---------------
12% Si, non-aging
130
450
------------45025040
Magnesium alloys
70
250
---------------
Unalloyed, electrolytic copper
100
340
---------------
Brass, bronze, red brass
90
310
---------------
Copper and copper alloys
Cu alloys, short-chipping
110
380
---------------
High-tensile, Ampco alloy
300
1010 ---------------
Annealed 200
680
---806040---------
Fe-based
Hardened 280
940
---806040---------
Heat-resistant alloys
Annealed 250
840
---806040---------
Ni or Co based
Hardened 350
1180 ---806040---------
Cast
320
1080 ---806040---------
Pure titanium
200
680
---806040---------
Titanium alloys
α and β alloys, hardened
375
1260 ---806040---------
β alloys
410
1400 ---806040---------
Tungsten alloys
300
1010 ---806040---------
Molybdenum alloys
300
1010 ---806040---------
Hardened and tempered
50HRC
-
---------------
Hardened steel
Hardened and tempered
55HRC
-
---------------
Hardened and tempered
60HRC
-
---------------
Chilled cast iron --------------- The recommended cutting data always refer to general cutting conditions. The actual selection should be adjusted according to machine rigidity, tool body and workpiece conditions and coolant. (f=mm/rev to be adjusted for insert radius) Hardened and tempered 55HRC -