New coated grades for Heat Resistant Alloys & Exotic Materials AC5005S / AC5015S / AC5025S • Wear Resistance of AC5015S New PVD Coating Technology Absotech®Bronze Reduces Wear
0.020
Competitor's Product A (S10 PVD)
AC5015S
█
Part Material: Insert: Cutting Conditions:
Inconel 718 (44HRC) CNMG432 v c = 131 SFM f = 0.004 IPR, a p =0.060 in, Wet
0.016
0.012
Conventional Tool A
13 Minutes Machining
13 Minutes Machining
l
0.008
█
Wear Resistance Compared to Conventional 2 x
0.004
█
█
█
0 5 10 15 20 25 30
35
Competitor's Product A
AC5015S
Cutting Time (min)
• Fracture Resistance of AC5015S Newly Developed Hard Base Material Suppresses Notch Wear
25
Hastelloy (22HRC) CNMG432 v c = 164 SFM f = 0.004 IPR, a p =0.060 in, Wet
Part Material: Insert: Cutting Conditions:
Fracture Resistance Compared to Conventional 1.5 x
20
15
10 Minutes Machining
13 Minutes Machining
10
5
0
AC5015S
Conventional Tool B
Competitor's Product B (S10 PVD)
Competitor's Product B
AC5015S
• Wear Resistance of AC5025S New PVD Coating Technology Absotech®Bronze Notch Wear
0.016
Competitor's Product C (S20 PVD)
█
Part Material: Insert: Cutting Conditions:
Inconel 718 (44HRC) CNMG432 v c = 131 SFM f =0.004 IPR, a p =0.060 in, Wet
AC5025S
Conventional Tool C
0.012
9 Minutes Machining
9 Minutes Machining
0.008
█
0.004
█
Wear Resistance Compared to Conventional 2.5 x
█
0
5
10
15
20
25
Competitor's Product C (S20 PVD)
AC5025S
Cutting Time (min)
• Fracture Resistance of AC5025S Newly Developed Hard Base Material Suppresses Boundary Defects
60
Hastelloy (22HRC) CNMG432 v c = 164 SFM f =0.004 IPR, a p =0.060 in, Wet
Part Material: Insert: Cutting Conditions:
Fracture Resistance Compared to Conventional 1.5 x
50
40
35 Minutes Machining
37 Minutes Machining
30
20
10
0
AC5025S
Conventional Tool D
Competitor's Product D (S20 PVD)
4
Competitor's Product D
AC5025S