INCH PINS, SLEEVES, BLADES Keyed THX Ejector Pins
•
Precision-machined flat on head keeps pin from rotating Made from superior quality thermal shock- resisting hotwork steel
• Core hardness of 50-55 HRC makes these pins ideal for use in die-cast dies or other high temperature applications • Annealed hot-forged heads provide uniform grain flow while allowing for easier machining
•
INFORMATION KEY: D = Pin Diameter H = Head Diameter K = Head Thickness L = Length
.031 R MAXIMUM
.004 FLAT ON HEAD FROM Ø D ±.002
40-45 HRC
Ø D
Ø H
K
L
Material: H-13 / 1.2344 / SKD61 Surface Treatment: Nitrided Surface Hardness: 65-74 HRC Core Hardness: 50-55 HRC
Keyed Ejector Pins – THXK
ITEM NUMBER PREFIX
D † PIN DIA TOLERANCES
L = LENGTH
H HEAD DIA
K HEAD THICK
Ø D PIN DIA
4
6
8
10
12
14
25
THXK07_*_ 3/32 THXK09_*_ 1/8 THXK10_*_ 9/64 THXK11_*_ 5/32 THXK13_*_ 3/16 THXK15_*_ 7/32 THXK17_*_ 1/4 THXK19_*_ 9/32 THXK21_*_ 5/16 THXK23_*_ 11/32 THXK25_*_ 3/8 THXK27_*_ 13/32 THXK29_*_ 7/16 THXK33_*_ 1/2 THXK35_*_ 9/16 THXK37_*_ 5/8 THXK41_*_ 3/4
(.0937) (.1250) (.1406) (.1562) (.1875) (.2187) (.2500) (.2812) (.3125) (.3437) (.3750) (.4062) (.4375) (.5000) (.5625) (.6250) (.7500) (.8750) (1.0000)
.250 .250 .250 .281 .375 .406 .437 .437 .500 .562 .625 .687 .687 .750 .812 .875
.125 .125 .125 .156 .187 .187 .187 .250 .250 .250 .250 .250 .250 .250 .250 .250 .250 .250 .250
–.0003 –.0006 EXCEPTION - PINS 25” LONG ARE
–.0003 –.0008
1.000 1.125 1.250
THX45_*_ THXK47_*_
7/8
1"
KEY TO CHART
Standard
Contact DME for quote
386
U.S. 800-626-6653 ■ Canada 800-387-6600 ■ DME@DME.net ■ www.DME.net ■ store.DME.net
Made with FlippingBook - professional solution for displaying marketing and sales documents online