Milling
Solid Carbide End Mill Pro Line Cutting Parameters
Square shoulder milling (Rough Machining)
1.0D
Materials
M110-2ES
0.1D
Tensile strength Rm(N/ mm²)
fz [mm/Tooth] Mill diameter [mm]
Brinell hardness (HB)
Cutting speed Vc(m/min)
Material classification
ISO
4
6 8
10 12 14
16
20
C ≤ 0.25%
Annealed
125
428
70~90 0.020 0.038 0.042 0.050 0.052 0.060 0.066 0.070
0.25 < C ≤ 0.55%
Annealed
190
639
70~85
0.020 0.038 0.042 0.050 0.052 0.060 0.066 0.070
0.25 < C ≤ 0.55%
Heat-treated 210
708
70~85
0.020 0.038 0.042 0.050 0.052 0.060 0.066 0.070
Unalloyed steel
Annealed
190
639
70~85
0.020 0.038 0.042 0.050 0.052 0.060 0.066 0.070
C > 0.55%
Heat-treated 300
1013
60~65
0.015 0.034 0.035 0.045 0.052 0.060 0.066 0.070
C > 0.55%
Free cutting steel (short-chip) Annealed
220
745
70~85
0.015 0.038 0.042 0.050 0.052 0.060 0.066 0.070
Annealed
175
591
70~85
0.020 0.038 0.042 0.050 0.052 0.060 0.066 0.070
P
Heat-treated
300
1013
50~60
0.015 0.034 0.035 0.045 0.048 0.055 0.057 0.060
Low-alloyed steel
Heat-treated
380
1282
50~60
0.015 0.034 0.035 0.045 0.048 0.055 0.057 0.060
Heat-treated
430
1477
45~50 0.015 0.030 0.030 0.040 0.045 0.050 0.050 0.055
Annealed
200
675
70~80
0.015 0.038 0.042 0.050 0.052 0.055 0.057 0.060
High-alloyed steel and high-alloyed tool steel
Hardened and tempered
300
1013
55~65
0.015 0.035 0.042 0.045 0.048 0.055 0.057 0.060
Hardened and tempered
400
1361
45~50 0.012 0.025 0.030 0.040 0.042 0.045 0.045 0.050
Ferritic/martensitic, annealed
200
675
55~70 0.015 0.038 0.042 0.050 0.052 0.055 0.057 0.060
Stainless steel
Martensitic, heat-treated
330
1114
40~55 0.015 0.035 0.035 0.045 0.048 0.055 0.057 0.060
Austenitic, quench hardened
200
675
35~45
0.018 0.038 0.041 0.043 0.053 0.055 0.057 0.058
M
Stainless steel
Austenitic, precipitation hardened (PH)
300
1013
35
0.012 0.030 0.032 0.035 0.040 0.043 0.045 0.050
Austenitic/ferritic, duplex
230
778
35~45
0.018 0.038 0.041 0.043 0.053 0.055 0.057 0.058
Ferritic
200
400
65~75
0.024 0.042 0.065 0.071 0.075 0.080 0.083 0.080
Malleable cast iron
Pearlitic
260
700
65~75
0.024 0.042 0.065 0.071 0.075 0.080 0.083 0.080
Low tensile strength
180
200
65~75
0.024 0.042 0.065 0.071 0.075 0.080 0.083 0.080
Grey cast iron
K
High tensile strength/austenitic
245
350
65~75
0.024 0.042 0.065 0.071 0.075 0.080 0.083 0.080
Ferritic
155
400
65~75
0.020 0.038 0.055 0.060 0.065 0.072 0.075 0.072
Nodular cast iron
Pearlitic
265
700
45~55 0.012 0.035 0.045 0.055 0.060 0.065 0.068 0.065
GGV(CGI)
230
400
65~75
0.020 0.038 0.055 0.060 0.065 0.072 0.075 0.072
Non-aging
30
-
Wrought aluminium alloys
Aged
100
340
≤ 12% Si, non-aging
75
260
Cast aluminium alloys
≤ 12% Si, aged
90
310
> 12% Si, non-aging
130
450
N
Magnesium alloys
70
250
Unalloyed, electrolytic copper
100
340
Brass, bronze, red brass
90
310
Copper and copper alloys
Cu alloys, short-chipping
110
380
High-tensile, Ampco alloy
300
1010
Annealed
200
680
Fe-based
Hardened
280
940
Heat-resistant alloys
Annealed
250
840
Ni or Co based
Hardened
350
1180
Cast
320
1080
S
Pure titanium
200
680
Titanium alloys
α and β alloys, hardened
375
1260
β alloys
410
1400
Tungsten alloys
300
1010
Molybdenum alloys
300
1010
Hardened and tempered
50HRC
-
40~45 0.020 0.030 0.040 0.050 0.050 0.060 0.070 0.090
Hardened steel
Hardened and tempered
55HRC
-
35~40 0.020 0.030 0.040 0.050 0.050 0.060 0.070 0.090
H
Hardened and tempered
60HRC
-
Chilled cast iron Hardened and tempered
50HRC
-
40~45 0.020 0.030 0.040 0.050 0.050 0.060 0.070 0.090
The cutting data are average recommended values. For special applications, adjustment is needed.