Milling
Solid Carbide End Mill Pro Line Cutting Parameters
0.5D
Slot milling
Materials
M116-4PS
D
Tensile strength Rm(N/ mm²)
fz [mm/Tooth] Mill diameter [mm]
Brinell hardness (HB)
Material classification
Cutting speed Vc(m/min)
ISO
6
8
10 12
16
20
C ≤ 0.25%
Annealed 125
428
80~100
0.035 0.055
0.069 0.082 0.088 0.089
0.25 < C ≤ 0.55%
Annealed 190
639
75~90
0.035 0.055
0.069 0.082 0.088 0.089
0.25 < C ≤ 0.55%
Heat-treated 210
708
75~90
0.035 0.055
0.069 0.082 0.088 0.089
Unalloyed steel
Annealed 190
639
75~90
0.035 0.055
0.069 0.082 0.088 0.089
C > 0.55%
Heat-treated 300
1013
60~70
0.030 0.050
0.060
0.072 0.075
0.078
C > 0.55%
Free cutting steel (short-chip) Annealed 220
745
75~90
0.035 0.055
0.069 0.082 0.088 0.089
Annealed
175
591
75~90
0.035 0.055
0.069 0.082 0.088 0.089
P
Heat-treated
300
1013
60~70
0.030 0.050
0.060
0.072 0.075
0.078
Low-alloyed steel
Heat-treated
380
1282
60~70
0.030 0.050
0.060
0.072 0.075
0.078
Heat-treated
430
1477
55~60
0.030 0.050
0.060
0.072 0.075
0.078
Annealed
200
675
75~85
0.035 0.055
0.069 0.082 0.088 0.089
High-alloyed steel and high-alloyed tool steel
Hardened and tempered
300
1013
60~70
0.030 0.050
0.060
0.072 0.075
0.078
Hardened and tempered
400
1361
55~60
0.030 0.050
0.060
0.072 0.075
0.078
Ferritic/martensitic, annealed
200
675
45~50
0.035 0.055
0.069 0.082 0.088 0.089
Stainless steel
Martensitic, heat-treated
330
1114
40~50
0.030 0.050
0.060
0.072 0.075
0.078
Austenitic, quench hardened
200
675
40~50
0.020 0.045 0.051 0.055
0.062
0.075
M
Stainless steel
Austenitic, precipitation hardened (PH)
300
1013
35
0.020 0.045 0.051 0.055
0.062
0.075
Austenitic/ferritic, duplex
230
778
40~50
0.020 0.045 0.051 0.055
0.062
0.075
Ferritic
200
400
70~80
0.035 0.055
0.069 0.082 0.088 0.089
Malleable cast iron
Pearlitic
260
700
70~80
0.035 0.055
0.069 0.082 0.088 0.089
Low tensile strength
180
200
70~80
0.035 0.055
0.069 0.082 0.088 0.089
Grey cast iron
K
High tensile strength/austenitic
245
350
70~80
0.035 0.055
0.069 0.082 0.088 0.089
Ferritic
155
400
70~80
0.035 0.055
0.069 0.082 0.088 0.089
Nodular cast iron
Pearlitic
265
700
65~75
0.035 0.055
0.069 0.082 0.088 0.089
GGV(CGI)
230
400
70~80
0.035 0.055
0.069 0.082 0.088 0.089
Non-aging
30
-
Wrought aluminium alloys
Aged
100
340
≤ 12% Si, non-aging
75
260
Cast aluminium alloys
≤ 12% Si, aged
90
310
> 12% Si, non-aging
130
450
N
Magnesium alloys
70
250
Unalloyed, electrolytic copper
100
340
Brass, bronze, red brass
90
310
Copper and copper alloys
Cu alloys, short-chipping
110
380
High-tensile, Ampco alloy
300
1010
Annealed 200
680
45~55
0.025 0.050 0.055
0.060
0.070 0.075
Fe-based
Hardened
280
940
35~45
0.020 0.045 0.051 0.055
0.062
0.075
Heat-resistant alloys
Annealed 250
840
45~55
0.020 0.045 0.051 0.055
0.062
0.075
Ni or Co based
Hardened 350
1180
35~45
0.020 0.045 0.051 0.055
0.062
0.075
0.075
Cast
320
1080
35~45
0.020 0.045 0.051 0.055
0.062
S
Pure titanium
200
680
45~55
0.020 0.045 0.051 0.055
0.062
0.075
Titanium alloys
α and β alloys, hardened
375
1260
30~40
0.015 0.035 0.041 0.045 0.052
0.065
β alloys
410
1400
20~25
0.015 0.035 0.041 0.045 0.052
0.065
Tungsten alloys
300
1010
35~45
0.020 0.045 0.051 0.055
0.062
0.075
Molybdenum alloys
300
1010
35~45
0.020 0.045 0.051 0.055
0.062
0.075
Hardened and tempered
50HRC
-
Hardened steel
Hardened and tempered
55HRC
-
H
Hardened and tempered
60HRC
-
Chilled cast iron Hardened and tempered
50HRC
-
The cutting data are average recommended values. For special applications, adjustment is needed.