SILICA REFRACTORY MORTARS
SILCAS A
SILCAS M
Silica based, ready mixed, refractory air setting mortar designed for setting and jointing dense firebricks. Maximum service temperature 1400°C /2550°F Examples of Applications: Kiln and furnace side walls constructed from special shapes or conventional bricks. Kiln and furnace roofs constructed from arch bricks. Smaller kiln cars subjected to low-thermal and mechanical stress, kiln car decks - jointed pre-fired blocks. General repair work such as installation of burners, peep-hole blocks, thermocouples etc.
White ready mixed, refractory air-setting mortar for setting and jointing insulating bricks. Maximum service temperature 1430°C /2600°F. Examples of Applications: Setting and jointing up to Grade 26 insulating bricks in a ceramic kiln and also extensively used in the precision casting industry in the investment casting lost wax process as an adhesive for sticking ceramic fibre blanket to ceramic shells.
T ECHNICAL D ATA Grade Bond Type Colour Application Technique P.C.E. Refractoriness. Temperature (Orton Cone) Grain Size Maximum service temperature Chemical Analysis (%) Al 2 O 2 SiO 2 Fe 2 O 3 K 2 O + Na 2 O Recommended Joint Thickness Quantity required per 1000 bricks
Silcas M Air setting White Trowelling / dipping 1491 C (16) <0.5mm 1430 C / 2600 F
Silcas A Air setting Grey Trowelling / dipping 1491 C (16) <0.5mm 1400 C / 2550 F
- 76.0
- 77.8
0.4 4.0 <3mm ~300 kg
0.4 3.0 <3mm ~300 kg
(230x114x76mm) Coverage per 1 kg
-
-
PACK Bucket
SIZE 25 kg
ON PALLET 40
WEIGHT 1000 kg
PALLET SIZE (mm) 1200 x 1000 x 1100
Note: The information only shows the most relevant product grades. This is not an exhaustive list of all the products which are available.
www.vitcas.com
16
Tel: +44 (0) 117 911 7895