Quick Spot Clear Quick Spot Urethane Clear is designed for fast curing spot and panel repairs, especially in cooler temperature environments. Quick Spot is very fast, buffs quickly and easily for quick delivery and great productivity. Mix Ratio 4:1 Part # Description Size 8910V Quick Spot Urethane Clear Gallon 8914V Quick Spot Urethane Clear Quart 8185V Urethane Clear Catalyst Normal Quart 8183V Urethane Clear Catalyst Normal Half Pint 8186V Urethane Clear Catalyst Slow Quart 8184V Urethane Clear Catalyst Slow Half Pint
Substrates Apply over basecoats, catalyzed enamels or urethanes. Follow basecoat prep recommendations. Mixing 4 part Quick Spot Clear 1 part Urethane Clear Catalyst Set Up Tech Info Tip/Needle: 1.3mm to 1.5mm Spot Air Pressure: 35 - 45 psi / HVLP 5 to 10 psi at cap Overall Air Pressure: 45 - 55 psi / HVLP 5 to 10 psi at cap Viscosity: #2 Zahn 18 - 21 seconds Film Build: 1.0 - 1.5 mils / full wet coat Coverage (@ 1 mil) 698 sq. ft. @ 1 mil Application Apply 1 medium coat followed by 1 full wet coat, 5-10 min. flash w/8185V, 10-15 min. flash w/8186V. Drying Air Dry w/8185V Panel(normal) w/8186V Overall (slow) Dust Free 10 min 15 min Tack Free 15 min 17 min Sand Time 2-5 hours 4-7 hours Recoat 12 hours 12 hours Pot Life 30 min 1 hour Force Dry - Purge for 15 to 20 minutes, 30 minutes at 140° F. Sand after cool down after cool down Recoat after cool down after cool down Buffing If necessary, sand with 1500 or finer grit. Buff with appropriate compound. Buffing is easiest when done within the first 12 hours following application.
Physical Data Volume Solids RTS
43.8%
Pot Life: VOC RTS:
30 minutes to 1 hour
Less than or equal to 4.2 lb./gallon
Humidity Resistance:
Excellent Excellent
Salt Spray Test:
Master Tips Always apply a minimum of two coats. Up to a 1/2 oz of accelerator may be added to reduced quart in cold environments, except when using 8185V. Clean spray equipment immediately! Do not use this clear as an “overall” clear. It is designed as a spot and panel clear. Buff within 12 hours of application.
Page 31
Made with FlippingBook flipbook maker