CLINICAL
CASE
Restored teeth 26 with BRILLIANT Crios A2 HT 27 with BRILLIANT Crios A2 LT Luting ONE COAT 7 UNIVERSAL with BRILLIANT EverGlow A2/B2
2. Prepare
1. Initial situation
6. Etching
4. Sandblasting
5. Bonding
3. CAD/CAM restoration (27)
7. Bonding
8. Light-curing
9. Luting
10. Light-curing
11. Final result
ORDER INFORMATION
BRILLIANT Crios
60020095 Intro Kit CEREC 12 Each 1 ×
60020097 Intro Kit CEREC 14 Each 1 ×
A2 LT 12, A3 LT 12, A3.5 LT 12, A2 HT 12, A3 HT 12
A2 LT 14, A3 LT 14, A3.5 LT 14, A2 HT 14, A3 HT 14
5 × 0.1 ml
ONE COAT 7 UNIVERSAL Single Dose
5 × 0.1 ml
ONE COAT 7 UNIVERSAL Single Dose
Disc (1 pc)
CEREC/inLab – 5 blocks
Low Translucent
High Translucent
Low Translucent
High Translucent
H 14
H 18
H 14
H 18
12
14
12
14
60019998 BL LT 12 60019999 A1 LT 12 60020000 A2 LT 12 60020001 A3 LT 12 60020002 A3.5 LT 12 60020003 B1 LT 12 60020004 B2 LT 12 60020005 B3 LT 12 60020006 C2 LT 12
60019985 BL LT 14 60019986 A1 LT 14 60019987 A2 LT 14 60019988 A3 LT 14 60019989 A3.5 LT 14 60019990 B1 LT 14 60019991 B2 LT 14 60019992 B3 LT 14 60019993 C2 LT 14
Bleach
60022899 A1 LT 14 60022900 A2 LT 14 60022901 A3 LT 14 60022902 A3.5 LT 14
60022886 A1 LT 18 60022887 A2 LT 18 60022888 A3 LT 18 60022889 A3.5 LT 18
60022907 A1 HT 14 60022908 A2 HT 14 60022909 A3 HT 14
60022894 A1 HT 18 60022895 A2 HT 18 60022896 A3 HT 18
60020007 A1 HT 12 60020008 A2 HT 12 60020009 A3 HT 12
60019994 A1 HT 14 60019995 A2 HT 14 60019996 A3 HT 14
A1
A2
A3
A3.5
60020010 B1 HT 12
60019997 B1 HT 14
B1
B2
B3
C2
ONE COAT 7 UNIVERSAL
60019538 ONE COAT 7 UNIVERSAL Intro Kit 1 × 5 ml ONE COAT 7 UNIVERSAL 1 × 2.5 ml Etchant Gel S
1 × 20 pcs. Application tips 1 × 50 pcs. Brushes black 1 × Mixing well 1 ×
Cover for mixing well
60019539 ONE COAT 7 UNIVERSAL Refill 1 × 5 ml ONE COAT 7 UNIVERSAL
60019540 ONE COAT 7 UNIVERSAL Single Dose 1 × 50 pcs. ONE COAT 7 UNIVERSAL Single Dose 1 × 50 pcs. Brushes black
7054
ONE COAT 7.0 Activator Kit
1 × 3 ml
ONE COAT 7.0 Activator
1 × 50 pcs. Brushes black
Coltène/Whaledent AG Feldwiesenstrasse 20 9450 Altstätten / Switzerland Tel. +41 (0)71 757 53 00 Fax +41 (0)71 757 53 01 info.ch@coltene.com
Coltène/Whaledent GmbH + Co. KG Raiffeisenstrasse 30 89129 Langenau / Germany Tel. +49 (0)7345 805 0 Fax +49 (0)7345 805 201 info.de@coltene.com
Coltène/Whaledent Inc. 235 Ascot Parkway Cuyahoga Falls, Ohio 44223 / USA
T +1 330 916 8800 F +1 330 645 8704 info.us@coltene.com
© 2018 Coltène/Whaledent AG - www.coltene.com
REINFORCED CAD/CAM COMPOSITE FOR PERMANENT RESTORATION
BRILLIANT Crios High performance – made brilliant
NEW Now also available as Disc
EFFICIENT
HANDLING
HIGHLY ACCURATE GRINDING PRECISION
BRILLIANT Crios is distinguished by superior precision. Even when ceramic materials have already started chipping, BRILLIANT Crios can still be ground with ease and precision in the case of extremely thin margins. This highly accurate grinding precision offers greater freedom of preparation.
IPS Empress CAD*
VITA Enamic*
BRILLIANT Crios
Lava Ultimate*
Ground tip 0.1 mm (Sirona inLab MC XL)
Source: C. Kopfmann et al., Eur. J. Prosthodont. Rest. Dent., EMDC Special, P21, 2015, Nuremberg | *Not a trademark of COLTENE
• Effortless polishing for fast gloss • No firing process required • Highly accurate grinding precision • Can be modified and repaired TIME SAVING AND COST EFFICIENT
Photo: Dr. Paulo Monteiro
BRILLIANT CRIOS FOR PERMANENT
AESTHETIC RESTORATIONS
REINFORCED COMPOSITE • High flexural strength supports permanent restorations • Shock-absorbing effect reduces stress transmission • Blends in well to provide natural aesthetics • Comparable wear resistance to glass-ceramic with less wear on human antagonist
EFFICIENT HANDLING • No firing process required • Can be modified and repaired • Highly accurate grinding precision • Effortless polishing for fast gloss* RELIABLE LUTING SYSTEM • Secure bonding with ONE COAT 7 UNIVERSAL • Compatible luting materials for all stated indications
SIZES
SHADES
12 14
Block
12 × 10 × 15 (mm) 14 × 12 × 18 (mm)
Low Translucent (LT) Bleach, A1, A2, A3, A3.5, B1, B2, B3, C2 High Translucent (HT) A1, A2, A3, B1
H14 H18
Disc
14 × 98.5 (mm) 18 × 98.5 (mm)
INDICATIONS
BRILLIANT Crios is the ideal choice for single tooth restorations in the anterior as well as posterior region of teeth. This includes all conventional indications such as inlays, onlays, crowns and veneers .
Inlay
Onlay
Crown
Veneer
*ALPEN ShapeGuard 2-Step Polisher; ALPEN Brush Plus Wide Cup
REINFORCED
COMPOSITE
The outstanding mechanical properties of BRILLIANT Crios are the result of controlled, stress-free thermal curing. The multimodal composition of dental glass and amorphous silica in combination with a reinforcing resin matrix make BRILLIANT Crios the ideal material for permanent single-tooth restorations.
The quality of BRILLIANT Crios is also reflected by its high flexural strength. The compact structure increases the material resistance and reduces the risk of fracture. A STRONG MATERIAL
BIAXIAL FLEXURAL STRENGTH
Measured in MPa
100 150 200 250 300 350 400
0 50
Source: internal data | *Not a trademark of COLTENE
SHOCK-ABSORBING EFFECT The dentin-like modulus of elasticity of BRILLIANT Crios reduces stress peaks during chewing, resulting in decreased risk of material fatigue. Due to its shock-absorbing effect, it is extremely well suited for implant restorations. As tooth substance and BRILLIANT Crios have a similar modulus of elasticity, loading stress is considerably reduced at the margins.
MODULUS OF ELASTICITY
Measured in GPa
Modulus of elasticity of natural dentin
60
50
40
30
20
10
Source: R. Böhner et al., #597, IADR 2015, Antalya, Turkey *Not a trademark of COLTENE
0
TWO-BODY WEAR
Wear material
Wear antagonist
Measured in µm
0 100 200 300 400 500 600 700
Source: Stawarczyk et al., J Mech Behav Biomed Mater 55, 1-11 (2015) | *Not a trademark of COLTENE
WEAR RESISTANT AND GENTLE AT THE SAME TIME Studies confirm the excellent abrasion resistance of BRILLIANT Crios. Nonetheless, the wear-resistant composite material proves to be especially kind to the antagonist teeth in comparison to ceramic restorations. BRILLIANT Crios is suitable as a permanent restoration material – even under considerable chewing forces – and thus offers the best of both worlds.
BRILLIANT Crios blends in well and conveys natural aesthetics. A broad spectrum of 13 shades in two translucencies perfectly covers the needs in the anterior as well as posterior region of teeth. Immediately after grinding, BRILLIANT Crios displays an extremely homogeneous surface structure. The restoration can therefore be brought to a high gloss very quickly. Easy repolishing, for example during prophylaxis, is possible at any time if required. NATURAL AESTHETICS WITH A GLOSSY RESULT
Composite has long been the gold standard in direct filling therapy. With BRILLIANT Crios, the well-proven dental material now enters indirect CAD/CAM restoration technology. Compared to ceramics, CAD/CAM composites for permanent restorations offer considerable advantages. BRILLIANT Crios Reinforced CAD/CAM composite for permanent restorations
RELIABLE
LUTING SYSTEM
As part of its adhesive filling therapy, COLTENE offers a complementary and proven luting system for BRILLIANT Crios. The key component of the luting concept is the universal adhesive ONE COAT 7 UNIVERSAL. The smooth BRILLIANT EverGlow composite or the dual-curing resin
cements DuoCem* and SoloCem offer indication- appropriate solutions, depending on the wall thickness of the restoration and the luting substrate, ranging from natural dentin to a metal abutment.
*DuoCem not available in Canada
BRILLIANT Crios max. wall thickness 3 mm sandblasted
BRILLIANT Crios max. wall thickness 5 mm sandblasted
BRILLIANT Crios max. wall thickness 5 mm sandblasted
ONE COAT 7 UNIVERSAL (mandatory)
Self-adhesive, dual-curing resin cement
Light-curing composite
Dual-curing resin cement
Bonding
Metals, ceramics
Tooth, composite
DuoCem ® Dual-curing resin cement
SoloCem ® Self-adhesive, dual-curing resin cement
BRILLIANT EverGlow® Light-curing composite
Ideal as luting material to dentin or composite for thin restoration walls.
Offers exceptional bonding values to dentin or composite, in particular for greater wall thickness.
Strong bonding to metal or ceramic abutments, without requiring an additional bonding step.
Wall thickness ≤ 3 mm
Wall thickness ≤ 5 mm
Wall thickness ≤ 5 mm
SECURE
BONDING
ONE COAT 7 UNIVERSAL
The monomers (red) contained in ONE COAT 7 UNIVERSAL penetrate into the polymerized resin matrix of BRILLIANT Crios.
ONE COAT 7 UNIVERSAL is matched perfectly to the BRILLIANT Crios components, resulting in strong anchorage and a reliable adhesion. This is why ONE COAT 7 UNIVERSAL adhesive is used in conjunction with BRILLIANT Crios.
Interlooping
Chain formation
Polymer chains are formed during polymerization of the monomers and these are anchored in the resin matrix.
The double bonds contained in the resin matrix form chains during polymerization of the monomers.
BRILLIANT Crios
ONE COAT 7 UNIVERSAL
SHEAR BOND STRENGTH WITH ONE COAT 7 UNIVERSAL Measured in MPa
30
The BRILLIANT EverGlow, DuoCem* and SoloCem luting materials demonstrate excellent bonding strengths to give a secure adhesion to BRILLIANT Crios.
20
10
*DuoCem not available in Canada
0
Source: internal data
FURTHER PROPERTIES
ONE COAT 7 UNIVERSAL is a light-curing one component universal adhesive. • Exceptional bonding values on enamel and dentin • Excellent marginal seal • Minimized postoperative sensitivity • For all application techniques (Self-Etch, Selective-Etch, Total-Etch)
*Methacryloyl-oxydecyl-dihydrogenphosphat