Introduction Composite manufacturing involves a diverse range of processes, ranging from wet lamination and room temperature resin infusion to high temperature and pressure curing of prepreg materials in an autoclave. Each manufacturing process is tailored to meet specific performance requirements. Our materials are engineered to support these critical steps, ensuring quality, efficiency, and reliability throughout the production process. These advanced solutions serve a wide array of industries, such as Aerospace, Automotive, Wind Energy, Marine, Sports and Leisure, and Infrastructure. Each sector relies on innovative materials to meet its unique challenges, from lightweight construction to durability in demanding environments. In this catalog, we present an overview of the key product categories essential for composite processing:
COMPOSITE PROCESSING MATERIALS
4
5
Breather Fabric Breather fabrics provide a pathway for gases, connecting the curing laminate to the vacuum manifold. They help maintain even pressure distribution during vacuum bagging, ensuring optimal laminate quality and uniformity. Additionally, they support consistent airflow, even under elevated temperatures and pressures, throughout the curing process.
3
Ancillaries This category includes connectors, small equipment, and other accessories that support composite processing, enhancing the efficiency and functionality of the entire operation. role in creating airtight seals during vacuum bagging, offering easy application and reliable performance in high- pressure environments. Sealant Tape / Adhesive Tape Sealant tapes play a critical varying temperatures and pressures, depending on the curing requirements. Vacuum Bagging Film Vacuum bags are used to create an air barrier and maintain consistent vacuum pressure during the manufacturing process. They ensure uniform pressure distribution and help achieve high- quality results. Different films are available, designed to withstand
Release Film The primary function of the release film in composite manufacturing is to ensure the cured part is easily released from the process materials pack. In some processes, perforated release films are used, which help control resin flow during infusion and allow gases to escape through the perforations, ensuring optimal curing and surface quality. Flow Media/ Combined Products Flow media enhance resin distribution during infusion, while combined products integrate multiple functions, simplifying the overall process and improving efficiency.
2
6-7
Feed and Vacuum Systems Integrated systems that ensure efficient resin delivery and vacuum control, essential for achieving optimal material infusion and curing throughout the production process. 9 Tubing & Spiral Wrap These components ensure secure hose connections and protect against damage, vital for maintaining the integrity of resin infusion processes. 10
8
1
Peel Ply/ Release Fabric
Textiles designed to create a textured surface or ensure clean release from resin systems, making post- processing easier and preventing resin adhesion.
By combining our expertise in composite materials with a deep understanding of industry needs, we deliver solutions that drive performance, efficiency, and innovation across diverse applications.
3
AEROVAC PRODUCT CATALOG
Peel Ply & Release Fabrics 1
PEEL PLY APPLICATION SUMMARY
UPPER USE TEMPERATURE C / F
FABRIC WEIGHT GSM / OZ/YD²
EASE OF REMOVAL
PRODUCT
MATERIAL
ROUGHNESS
APPROX. COST / M2
A100PS
Nylon 66
204 / 400
85 / 2.5
+++
++
$
A100PS PA6
Nylon 6
204 / 400
85 / 2.5
+++
+++
$-
B100
Nylon 66
204 / 400
58 / 1.7
+
++
$$
60001/60002
Polyester
204 / 400
85 / 2.5
+++
+
$$$
51789 SRB Nylon with release coating
232 / 450
62.7 / 1.85
++
++++
$$$$
Nylon 66 with release coating
B4444
204 / 400
60 / 1.77
+
++++
$$$$
RELEASE FABRIC APPLICATION SUMMARY
UPPER USE TEMPERATURE C / F
EASE OF REMOVAL
PRODUCT
MATERIAL
THICKNESS POROUS
APPROX. COST / M2
200TFP
Fiberglass coated PTFE - Porous
290 / 550
3 mil
Yes
++++
$
200TFNP
Fiberglass coated PTFE - Non Porous
290 / 550
3 mil
No ++++
$$
Toolcoat 805 - A Fiberglass coated PTFE + Acrylic adhesive
204 / 400
5 mil
No ++++
$$$
Toolcoat 805 - S Fiberglass coated PTFE + Silicone adhesive
290 / 550
5 mil
No ++++
$$$$
Toolcoat 807 - A Fiberglass coated PTFE + Acrylic adhesive
204 / 400
7 mil
No ++++
$$$$
Toolcoat 807 - S Fiberglass coated PTFE + Silicone adhesive
290 / 550
7mil
No ++++
$$$$$
*The price comparison in the table is not compared with other product classes.
4
Peel Ply & Release Fabrics
A100PS-PA6 A100PS-PA6 is a Nylon 6 peel ply with an areal weight of 2.5 oz/yd² (85 gsm), available in natural with red stripes for improved visibility during removal. Suitable for use up to 400°F (204°C), it is compatible with epoxy resin for strong adhesive bonding, while performance with prepreg and polyester resin should be validated through testing. Thanks to its Nylon 6 composition, A100PS- PA6 provides a more cost-effective alternative to Nylon 66 peel plies for standard infusion and oven-cure applications.
Narrow width hot knife slitting is available.
Application: Infusion and oven cure Resin: Polyester, Vinyl Ester and Epoxy
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
846516
PP-A100PS/PA6-WHT-85-1524-274
60 in (1524 mm)
300 yd (274 m)
A100PS A100PS is a Nylon 66 peel ply with an areal weight of 2.5 oz/yd² (85 gsm), available in natural or natural with red stripes for better visibility during removal. It strips cleanly from cured parts and is often supplied with red tracer yarn to prevent residue. Designed for use up to a maximum service temperature of 400°F (204°C), it is compatible with epoxy resin for strong adhesive bonding. Performance with prepreg and polyester resin may vary and should be tested.
Application: Infusion and oven cure Resin: Polyester, Vinyl Ester and Epoxy
Narrow width hot knife slitting is available.
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
676141
PP-A100PSI-WHT-85-1524-274-NA
60 in (1524 mm)
300 yd (274 m)
682894
PP-A100PSI-WHT-85-102-274
4 in (102 mm)
300 yd (274 m)
B100
B100 is a premium Nylon 66 peel ply with a fine weave construction and an areal weight of 1.7 oz/yd² (58 gsm), designed to provide a fine surface finish on composite parts. It is suitable for use up to a maximum service temperature of 400°F (204°C) and is fully compatible with epoxy resin for reliable surface preparation and secondary bonding. When used with phenolic resins or phenolic-based prepreg systems, performance should be validated through testing, as acidic components in these resin systems may cause fiber degradation. Application: Infusion, oven and autoclave cure Resin: Polyester, Vinyl Ester and Epoxy
Narrow width hot knife slitting is available.
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
676138
PP-B100-NAT-60-1524-91-NA
60 in (1524 mm)
100 yd (91 m)
5
AEROVAC PRODUCT CATALOG
Peel Ply & Release Fabrics
60001 and 60002
60001 is a 100% polyester peel ply with an areal weight of 2.5 oz/yd² (85 gsm), providing a medium surface finish for vacuum bag lay-up composites and metal-to-metal bonding. It is suitable for use up to 400°F (204°C) and is compatible with epoxy, phenolic, and BMI resins. 60002 offers the same performance, with black identification stripes for improved visibility during removal. Application: Oven and autoclave cure cycles Resin: Epoxy, Phenolic and BMI
Narrow width hot knife slitting is available.
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
COLOR
678862
PP-60001-NAT-85-1524-274
60 in (1524 mm)
300 yd (274 m)
Natural
Natural with black stripes
232300
60002-060 47” NATURAL PEEL PLY NA 47 in (1194 mm)
300 yd (274 m)
51789 and 51789 SRB 51789 is a 100% Nylon 66 peel ply with a fine weave construction and an areal weight of 1.85 oz/yd² (63 gsm), designed for vacuum bag lay-up composites and metal-to-metal bonding. It provides a fine surface finish for primary and secondary bonding and is suitable for use up to 450°F (232°C). 51789 SRB offers the same base construction, with the addition of an inert, heat-stabilized, cross-linked polymer release coating for enhanced performance and easier release.
Narrow width hot knife slitting is available.
Application: Infusion, oven and autoclave cure cycles Resin: Polyester, Vinyl Ester, Epoxy, Phenolic and BMI
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
COLOR
678879
PP-51789-NAT-63-1524-274-NA
60 in (1524 mm)
300 yd (274 m)
Natural
676394
PP-51789SRB-BLU-63-1524-91
60 in (1524 mm)
100 yd (91 m )
Blue
B4444 B4444 is a lightweight silicone-coated nylon peel ply with an areal weight of 1.77 oz/yd² (60 gsm), designed for infusion, oven, and autoclave cure cycles. The heat-cured silicone coating provides excellent release properties, ensuring easy removal from cured laminates, while being fully polymerized to minimize the risk of silicone transfer to the molded part. The material is suitable for use up to a maximum service temperature of 400°F (204°C). Application: Infusion, oven and autoclave cure cycles Resin: Polyester, Vinyl Ester and Epoxy
Narrow width hot knife slitting is available.
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
COLOR
676142
PR-B4444-GRN-60-1524-91
60 in (1524 mm)
100 yd (91 m )
Green
6
Peel Ply & Release Fabrics 200TFP and 200TFNP
200TFP and 200TFNP are PTFE-coated woven fiberglass release fabrics, distinguished by one being porous (200TFP) and the other non-porous (200TFNP). These materials are designed for applications up to 550°F (290°C) and ensure effortless release of cured laminates by preventing adhesion between the composite material and the mold surface, enabling clean removal without damage. The porosity of 200TFP, with an areal weight of 1.8–2.1 oz/yd² (53–75 gsm), facilitates evacuation of excess resin and volatiles during processing, while 200TFNP, with an areal weight of 4.0 oz/yd² (132 gsm), is non-porous and ideally suited for metal-bond and controlled resin bleed applications.
Narrow width hot knife slitting is available.
Application: Infusion, oven and autoclave cure cycles Resin: Polyester, Vinyl Ester, Epoxy, Phenolic and BMI
PRODUCT CODE
DESCRIPTION
THICKNESS
WIDTH
LENGTH
678144
PR-200TFNP-TAN-76-965-91
3 mil (76 microns)
38 in (965 mm)
100 yd (91 m)
676145
PR-200TFP-BRN-76-1270-91
3 mil (76 microns)
50 in (1270 mm)
100 yd (91 m)
TOOLCOAT (TC805 / TC807)
Toolcoat is a self-adhesive tool release fabric made of fiberglass coated with non-porous PTFE, designed to facilitate the separation of composite parts from molds or tools and enable easy removal without surface damage. The material is inert to most chemicals and environmental factors and is suitable for infusion, oven, and autoclave cure cycles. Maximum service temperature depends on the adhesive type: acrylic adhesive systems are rated up to 400°F (204°C), while silicone adhesive systems are rated up to 550°F (290°C).
Narrow width hot knife slitting is available.
Application: Infusion, oven and autoclave cure cycles Resin: Polyester, Vinyl Ester, Epoxy, Phenolic and BMI
TOTAL THICKNESS
ADHESIVE TYPE Acrylic adhesive Acrylic adhesive Silicone adhesive Silicone adhesive
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
PR-TC805A-BRN-127-914-16-TFE- N-AC
232933
36 in (914 mm)
52 ft (15.8 m) 5 mil (127 µm)
232930 PR-TC807A-BRN-178-914-16.5-TFE- N-AC 36 in (914 mm) 54 ft (16.5 m) 7 mil (178 µm)
PR-TC805S-BRN-127-914-33 TFE- N-SL
698255
36 in (914 mm)
108 ft (33 m) 5 mil (127 µm)
686891 PR-TC807S-BRN-178-914-16.5-TFE- N-SL 36 in (914 mm) 54 ft (16.5 m) 7 mil (178 µm)
7
AEROVAC PRODUCT CATALOG
Release Film 2
RELEASE FILM APPLICATION SUMMARY
UPPER USE TEMPERATURE C / F
TENSILE STRENGTH MPA TD:5801 / MD:9427 PSI
RELEASE PERFOR- MANCE
APPROX. COST/ M2
ELONGATION %
CONFORM- ABILITY
PRODUCT MATERIAL
APPLICATION
MARKET
RESIN
Infusion, oven and autoclave cure cycles
Polyester, Vinyl Ester, Epoxy, Phenolic and BMI Polyester, Vinyl Ester and Epoxy Polyester, Vinyl Ester, Epoxy, Phenolic and BMI Polyester, Vinyl Ester, Epoxy, Phenolic and BMI Polyester, Vinyl Ester, Epoxy, Phenolic and BMI Polyester, Vinyl Ester, Epoxy, Phenolic and BMI
150 C / 302 F 120 C / 248 F
TD:800 / MD:500 %
A2300 PP
++++
+
$$
All
Marine and Wind Aerospace, Defense
A2400 PE
6526 PSI
560%
++++
++
$
Infusion
Autoclave cure cycles
A2500 PMP 204 C / 400 F
4351 PSI
285%
+
+++
$$
260 C / 500 F
Autoclave cure cycles
Aerospace, Defense
A5000 FEP
3500 PSI
300%
++++
++++ $$$$
TD:6000 / MD:10000 PSI
260 C / 500 F
Autoclave cure cycles
Aerospace, Defense Auto, Aerospace, Defense
A6200
ETFE
350%
+++
+++
$$$
316 C / 600 F
Autoclave cure cycles
MR1 PTFE
4300 PSI
400%
+++++ +++++ $$$$$
COMMON PATTERNS
1" (25.4mm)
P
P3
P31
0.50" (12.6mm)
0.25" (6.3mm)
1" (25.4mm)
0.05" (12.6mm)
0.25" (6.3mm)
0.045" (1.143 mm)
0.015" (0.38 mm)
0.015" (0.38 mm)
P16 Hot
P1
MP25
0.5" (12.7mm)
0.078" (2mm)
0.078" (2mm)
0.24" (6mm)
0.5" (12.7mm)
0.12" (3mm)
0.016" (0.40 mm)
0.045" (1.143 mm)
0.005" (0.127 mm)
8 Other perforations are also available. Please contact the technical team for further support.
Release Film
A2300
A2300 is a cast co-extruded polypropylene-based film developed for release applications in composite infusion processes and is available in both perforated and non-perforated configurations. In the wind blade repair market, the non-perforated version can also be used as a bagging and consolidation film for small repairs using dry lay-up processes, supporting laminate consolidation and resin control during cure.
Application: Infusion, oven and autoclave cure cycles Resin: Polyester, Vinyl Ester, Epoxy and Phenolic
COLOR
TENSILE
TOTAL THICKNESS
PERFORATION TYPE Perforated (P3) Non- perforated
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
ORANGE TD: 5801 / MD: 9427 PSI ELONGATION MAX USE TEMP. 300% 302 F / 150 C
60 in (1524 mm) 60 in (1524 mm)
333 yd (305 m) 333 yd (305 m)
1 mil (30 µm) 1 mil (30 µm)
676355 RF-A2300-ORG-30-1524-305-P3-SHT
AUS RF-A2300-ORG-30-1524-305- NP-NP-FNS
841523
Available in 1 and 2 mil thicknesses up to 78 in. wide. Custom narrow width slitting is available to 2 in. minimum. Available with a range of perforation patterns.
A2400
A2400 is a blown co-extruded polyethylene-based film specifically developed for release applications in composite infusions. Application: Infusion Resin: Polyester, Vinyl Ester and Epoxy
TOTAL THICKNESS
PERFORATION TYPE Perforated (P16)
COLOR TENSILE TD: 6528 / MD: 6528 PSI ELONGATION MAX USE TEMP. 560% 248 F / 120 C ORANGE & RED
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
RF-A2400-ORG-25-1550-500-HOT- P16-FNS-SHT
61 in (1550 mm)
547 yd (500 m)
1 mil (25 µm)
685028
Available in 1 and 2 mil thicknesses up to 78” wide. Custom narrow width slitting is available to 2” minimum. Available with a range of perforation patterns.
A2500
A2500 is a Polymethylpentene (PMP) release film used in the processing of flat or simple curvature components. It offers a low-cost alternative to other high-temperature Aerospace-qualified films and is PFAS free, ensuring excellent release from all common resin systems. Application: Autoclave cure cycles Resin: Polyester, Vinyl Ester, Epoxy, Phenolic and BMI
TOTAL THICKNESS
PERFORATION TYPE Non- perforated Perforated (P3)
COLOR TENSILE MPA: 4351 ELONGATION MAX USE TEMP. 285% 400 F / 204 C PINK & RED
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
RF-A2500-RED-30-1350-400-NP- FNS-SHT AUS RF-A2500-RED-30-1350-400- PIN-P3-FNS
53 in (1350 mm) 53 in (1350 mm)
437 yd (400 m) 437 yd (400 m)
2 mil (30 µm) 2 mil (30 µm)
843148
849637
Available in 1.5 and 2 mil thicknesses up to 80” wide. Custom narrow width slitting is available to 2” minimum. Available with a range of perforation patterns.
TD: Transverse Direction MD: Machine Direction MPa: Megapascal
9
AEROVAC PRODUCT CATALOG
Release Film
A5000
A5000 is a high-temperature fluoropolymer release film based on flourinated ethylene propylene - FEP. A staple in the Aerospace industry for decades, A5000 boasts numerous Aerospace OEM approvals. Additionally, this film can be treated to make one side bondable for use in conjunction with reusable silicone bagging. Application: Autoclave cure cycles Resin: Polyester, Vinyl Ester, Epoxy, Phenolic and BMI
TOTAL THICKNESS
PERFORATION TYPE Non- perforated Perforated (P3) Perforated (P)
COLOR
TENSILE
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
VIOLET, WHITE, CLEAR, & RED
3500 PSI
RF-A5000-VLT-25-1524-183-NP-NP- FNS-SHT RF-A5000-VLT-25-1524-183-PIN-P3- FNS-SHT RF-A5000-VLT-25-1524-183-PUN-P- FNS-SHT
60 in (1524 mm) 60 in (1524 mm) 60 in (1524 mm)
200 yd (183 m) 200 yd (183 m) 200 yd (183 m)
1 mil (25 µm) 1 mil (25 µm) 1 mil (25 µm)
232544
ELONGATION
MAX USE TEMP.
836604
300%
500 F / 260 C
836605
Available in 1 and 2 mil thicknesses up to 80” wide. Custom narrow width slitting is available to 2” min. Available with a range of perforation patterns.
A6200
A6200 is a high temperature flouropolymer release film base on Ethylene Tetrafluoroethylene (ETFE).This film is approved by various Aerospace OEMs. Application: Autoclave cure cycles Resin: Polyester, Vinyl Ester, Epoxy, Phenolic and BMI
TOTAL THICKNESS
PERFORATION TYPE Non- perforated Perforated (P3)
COLOR
TENSILE
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
BLUE, CLEAR, & RED ELONGATION
TD: 6,000/ MD:10,000 PSI
RF-A6200-BLU-25-1525-127-NP-NP- FNS-SHT RF-A6200-BLU-25-1525-127-PIN-P3- FNS-SHT
60 in (1525 mm) 60 in (1525 mm)
139 yd (127 m) 139 yd (127 m)
1 mil (25 µm) 1 mil (25 µm)
698253
MAX USE TEMP. 350% 500 F / 260 C
696516
Available in .0005, .0006, .001 and .002” thicknesses. Custom narrow width slitting is available to 2” min.. Available with a range of perforation patterns.
MR1
MR1 is a high-performance fluoropolymer film based on polytetrafluoroethylene (PTFE), renowned for delivering superior performance and surface finish on cured laminates. Application: Autoclave cure cycles Resin: Polyester, Vinyl Ester, Epoxy, Phenolic, BMI and Polyimide
TOTAL THICKNESS
PERFORATION TYPE Non- perforated
COLOR
TENSILE 4,300 PSI
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
BLUE, RED, & BEIGE ELONGATION
RF-MR1-BLU-25-1219-152-NP-NP- FNS-SHT
48 in (1219 mm)
167 yd (152 m)
1 mil (25 µm)
676156
MAX USE TEMP. 400% 599 F / 315 C
Available in 1 and 2 mil thicknesses up to 48” wide. Custom narrow width slitting is available to 2” min. Available with a range of perforation patterns.
10
Flow Media/Combined Products 3
FLOW MEDIA & COMBINED PRODUCTS SUMMARY
FUNCTION
UPPER USE TEMPERATURE °C/°F
DENSITY GSM / OZ/YD²
APPROX. COST / M2
PRODUCT
MATERIAL
FLOW MEDIA
BREATHER PEEL PLY
RELEASE
VI1
HDPE
120 / 248
X
150 / 4.42
$$
Vi5
PET
200 / 392
X
100 / 3
$$
Vi10
PP
150 / 300
X
100 / 3
$
Infuply 2
HDPE + PE
120 / 248
X
X
175 / 5.16
$$$
Combi 1
HDPE + PE + PA 120 / 248
X
X
X
260 / 7.67
$$$$
COMPOFLEX ® 150
PP
145 / 293
X
X
150 / 4.4
$$$
COMPOFLEX ® SB RF3
PP + PE
145 / 293
X
X
X
335 / 9.9
$$$$$
VI1
The Flow Media VI1 is a 3D knitted infusion mesh made from HDPE, designed for vacuum- assisted resin infusion. It ensures controlled resin flow and continuous air evacuation, ideal for complex tooling geometries. Application: Infusion Resin: Polyester, Vinyl Ester and Epoxy
COLOR
WEIGHT
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
BLUE
4.42 OZ/YD 2
59 in (1500 mm)
109 yd (100 m)
697633
AEU FM-VI1-BLU-150-1500-100-SHT
MATERIAL MAX USE TEMP. POLYETHYLENE 248 F / 120 C
Available in a standard size of 59” wide with custom narrow width slitting available. Wider widths are available.
11
AEROVAC PRODUCT CATALOG
Flow Media/Combined Products
Vi5
Vi10 DESCRIPTION Vi10 is a an extruded polypropylene mesh with a diamond pattern ideally suited for resin flow in vacuum infusion processes. Its softness does not damage vacuum bags during use and its geometric pattern allows for consistent controlled resin flow across a laminate. Application: Infusion Resin: Polyester, Vinyl Ester and Epoxy COLOR WEIGHT GREEN 3 OZ/YD 2 MATERIAL MAX USE TEMP. POLYPROPYLENE 300 F / 149 C WIDTH LENGTH FM-VI10-GRN-112-1040-107-SHT 41 in (1040 mm) 117 yd (107 m) DESCRIPTION Vi5 is a knitted polyester mesh in a 3D pattern designed for use in the vacuum assisted resin infusion. Due to its composition and compatibility with Polyester and Vinyl Ester resins, it can be applied in the middle of glass fiber layers. It is ideal for use in areas of complex geometry and high temperature applications. Application: Infusion Resin: Polyester, Vinyl Ester and Epoxy COLOR WEIGHT WHITE 3 OZ/YD 2 MATERIAL MAX USE TEMP. PET 392 F / 200 C WIDTH LENGTH FM-VI5-WHT-100-1200-100 47 in (1200 mm) 109 yd (100 m)
PRODUCT CODE
698352
Available in a standard size of 47” wide with wider widths available by special order.
PRODUCT CODE
676151
Available in a standard size of 41” wide with custom narrow width slitting available. Wider widths are available.
INFUPLY2
DESCRIPTION Infuply2 is a combination of high comfortability Vi1 knitted infusion mesh and perforated release film A2400 with P16 perforation pattern. It reduces layup time and complexity and strips clean from the laminate surface. Application: Infusion Resin: Polyester, Vinyl Ester and Epoxy COLOR WEIGHT WIDTH LENGTH
PRODUCT CODE
BLUE MESH / ORANGE FILM
5.16 OZ/YD 2
57 in (1450 mm)
109 yd (100 m)
690307
INFUPLY2 VI1+A2400HP16-1450-100
MATERIAL MAX USE TEMP. POLYETHYLENE 248 F / 120 C
Available in a standard width of 57” wide
12
Flow Media/Combined Products
COMBI1
DESCRIPTION Vac-Ply Combi1 combines perforated release film, knitted infusion mesh and nylon peel ply all in one material. It reduces lay up time and complexity and easily conforms to complex parts. Its multi-layer construction can strip from the cured part in two different ways. One by pulling the release film and mesh, leaving the peel ply as temporary protection for the laminate, or by removing all three layers. Application: Infusion Resin: Polyester, Vinyl Ester and Epoxy COLOR WEIGHT WIDTH LENGTH
PRODUCT CODE
BLUE MESH / ORANGE FILM / WHITE RED STRIPED PEEL PLY BLUE MESH / ORANGE FILM / WHITE RED STRIPED PEEL PLY
61 in (1560 mm)
109 yd (100 m)
232698
CM-COMBI1-VI1+A2400HP16-A100PS-1560-100
7.67 OZ/YD 2
Available 61 inch wide rolls with the different layers staggered to allow for easier separation if desired.
MATERIAL
MAX USE TEMP.
POLYETHYLENE MESH & RELEASE FILM WITH NYLON PEEL PLY
248 F / 120 C
COMPOFLEX ® 150 Compoflex 150 is a breather and release film, used to control flow rate and release consumables from a composite laminate. Compoflex® 150 generates a highly smooth surface, ideal for painting composite laminate. Application: Infusion and oven Resin: Polyester, Vinyl Ester, Epoxy and Phenolic COLOR WEIGHT WHITE 4.4 OZ/YD 2 MATERIAL MAX USE TEMP. POLYPROPYLENE 293 F / 145 C COMPOFLEX ® SB RF3 Compoflex® SB RF 3 is a breather, release film, and flow mesh used to control the flow rate and release consumables from a composite laminate. It generates a highly rough and textured surface, ideal for secondary bonding and painting composite laminates. Compoflex® SB can reduce or eliminate the need for sanding or abrasion. Best results are achieved with epoxy resin, but we always recommend testing. Application: Infusion Resin: Polyester, Vinyl Ester, Epoxy and Phenolic COLOR WEIGHT WHITE AND YELLOW 9.8 OZ/YD 2 MATERIAL MAX USE TEMP. POLYPROPYLENE & POLYETHYLENE 293 F / 145 C DESCRIPTION WIDTH LENGTH FBT COMPOFLEX 150 60 in (1520 mm) 67 yd (61 m) DESCRIPTION WIDTH LENGTH FBT COMPOFLEX SB RF 3 60 in (1520 mm) 67 yd (61 m)
PRODUCT CODE
836718
Custom narrow width slitting and wider widths are available.
PRODUCT CODE
836723
Custom narrow width slitting and wider widths are available.
13
AEROVAC PRODUCT CATALOG
Breather 4
A3000/RC3000
A3000 / RC3000 breather fabrics are nonwoven materials available in polyester and nylon, designed to ensure efficient air evacuation and vacuum support during infusion, oven, and autoclave cure cycles. Polyester breathers provide robust, versatile performance, while nylon breathers generally offer higher and more consistent air flow over extended cure times, making them well suited for long or high-temperature cycles. FR options are available with flame- retardant additives for use in non-inert curing atmospheres and to help meet vertical burn requirements. All variants are highly conformable for complex geometries.
Application: Infusion, oven and autoclave cure cycles Resin: Polyester, Vinyl Ester, Epoxy, Phenolic and BMI
Polyester
PRODUCT CODE
STANDARD PRODUCT
CONSTRUCTION
WEIGHT
WIDTH
LENGTH
COLOR WEIGHT WHITE 4 OZ/YD² UP TO 20 OZ/YD² MATERIAL MAX USE TEMP. POLYESTER 400 F / 204 C
60 in (1524 mm) 60 in (1524 mm) 60 in (1524 mm) 60 in (1524 mm) 60 in (1524 mm) 60 in (1524 mm) 60 in (1524 mm) 60 in (1524 mm) 60 in (1524 mm)
100 yd (91 m) 50 yd (46 m) 50 yd (46 m) 25 yd (23 m) 100 yd (91 m) 50 yd (46 m) 50 yd (46 m) 50 yd (46 m) 50 yd (46 m)
676172
BR-A3000-WHT-136-1524-91
Polyester
4 oz/yd² (136 g/m²)
676176
BR-A3000-WHT-237-1524-46
Polyester
7 oz/yd² (237 g/m²)
676170
BR-RC3000-WHT-339-1524-46
Polyester
10 oz/yd² (339 g/m²)
232325
BR-RC3000-WHT-678-1524-23
Polyester
20 oz/yd² (678 g/m²)
Nylon
232515
BR-A3000FR-WHT-136-1524-91
Polyester (FR)
4 oz/yd² (136 g/m²)
COLOR WHITE
WEIGHT
4 OZ/YD² UP TO 13 OZ/YD² MAX USE TEMP.
232892
BR-A3000FR-WHT-237-1524-46
Polyester (FR)
7 oz/yd² (237 g/m²)
MATERIAL
676175 BR-RC3000NB-WHT-203-1524-46
Nylon
6 oz/yd² (203 g/m²)
NYLON
450 F / 232 C
232894 BR-RC3000NB-WHT-339-1524-46
Nylon
10 oz/yd² (339 g/m²)
691476 BR-RC3000NB-WHT-441-1524-46
Nylon
13 oz/yd² (441 g/m²)
Available in a standard size of 60” wide with wider widths available by special order.
4819
4819 is a highly conformable breather designed for complex composite cures. Made from 100% high-melt polyester, it offers excellent tensile strength and reduces bridging on complex surfaces, ensuring an optimal resin-to-fiber ratio in multi-layer applications.
Application: Infusion, oven and autoclave cure cycles Resin: Polyester, Vinyl Ester, Epoxy, Phenolic and BMI
COLOR WHITE
WEIGHT 2 OZ/YD 2
PRODUCT CODE
STANDARD PRODUCT
CONSTRUCTION WEIGHT
WIDTH
LENGTH
MATERIAL POLYESTER
MAX USE TEMP.
2 oz/yd² (68 g/m²)
48 in (1219 mm)
250 yd (229 m)
400 F / 204 C
232911 BR-4819-WHT-68-1219-229 Polyester
Available in a standard size of 48” wide with wider widths available by special order.
14
Bagging Film 5
BAGGING FILM APPLICATION SUMMARY
UPPER USE TEMPERATURE C / F
TENSILE STRENGTH
ELONGATION %
CONFORM- ABILITY
APPROX. COST / M2
PRODUCT
MATERIAL
APPLICATION
MARKET
RESIN
Autoclave cure cycles
Aerospace, Defense Automotive, Aerospace, Defense Aerospace, Defense, Automotive Aerospace, Defense, Automotive
Polyester, Vinyl Ester, Epoxy and Phenolic*
HS8171
Nylon
204 C / 400 F 15000 PSI
400%
++
$$$
Infusion, Oven and Autoclave cure cycles
Polyester, Vinyl Ester, Epoxy and Phenolic
SV4000
Nylon
212 C / 414 F 15228 PSI
500%
++++
$$+
Most common resin system
SV250 Polyurethane 135 C / 275 F 11000 PSI
500%
+++++ $$$$$ Compaction or De-bulk
HS8171 Quick Draw
Most common resin system
Nylon
204 C / 400 F 14000 PSI
415%
++
$$$$$ Compaction or De-bulk
Wet lay-up and infusion Wet lay-up and infusion Wet lay-up and infusion Infusion, Oven and Autoclave cure cycles Autoclave and Oven cure cycles
500G Multilayered Polymer 150 C / 302 F 7200 PSI
460%
+++
$$
All markets Polyester, Vinyl Ester and Epoxy
Marine and Wind (Nacelles) Marine and Wind (Nacelles) Aerospace, Wind, Industrial Aerospace, Defense
Polyester, Vinyl Ester and Epoxy
205B Multilayered Polymer 120 C / 248 F 6500 PSI
600%
+++
$
Polyester, Vinyl Ester and Epoxy
200G Multilayered Polymer 120 C / 248 F 6500 PSI
500%
+++
$
Polyester, Vinyl Ester, Epoxy and Phenolic Epoxy, Phenolic, BMI and High-temp thermoplastics
450V
Nylon
170 C / 338 F 6537 PSI
400%
+++
$$
UHT750 Polyimide 426 C / 800 F 39160 PSI
— ++
$$$$$$
HOW DIFFERENT PRODUCTS ARE MEASURED
GUSSETED CENTER SLIT (GSC)
CENTERFOLD CENTER SLIT (CSC)
SHEET (SHT)
V-SHEET (LTX)
TUBE (LFT)
WIDTH MEASUREMENT
WIDTH MEASUREMENT
WIDTH MEASUREMENT
WIDTH MEASUREMENT
WIDTH MEASUREMENT
15
AEROVAC PRODUCT CATALOG
Bagging Film
Four Important Cost Considerations: The price of vacuum bags is influenced not only by the composition of the film but also by four other factors: thickness, width, length, and packaging. 1. Thickness. Films with a thickness of 3 mil have a higher cost compared to those with a thickness of 2 mil due to the increased quantity of raw material per square meter. 2. Width. Films with widths exceeding 8 to 10 meters require specialized manufacturing and handling equipment, which may result in higher prices in some cases. 3. Length. Film rolls with short lengths cannot be manufactured directly on the blown film extrusion line, leading to increased costs due to secondary operations. 4. Packaging. The price may vary depending on the packaging method, as outlined to the right.
VFS ($$$)
This packaging is designed for low volume sales, featuring individual cardboard tube protection for each roll.
VFS2 ($)
A protective cardboard box over the completed pallet. Packaging best suited for sale in full pallet quantities.
HS8171
HS8171 is the traditional co-extruded modified nylon film, which has been qualified to numerous Aerospace manufacturer specifications. Application: Autoclave cure cycles Resin: Polyester, Vinyl Ester, Epoxy and Phenolic*
TOTAL THICKNESS
FOLD TYPE
COLOR GREEN
TENSILE 15,000 PSI
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
38 in (965 mm)** 50 in (1270 mm)** 62 in (1575 mm)** 72 in (1828 mm)** 74 in (1880 mm) (open)
333 yd (305 m) 333 yd (305 m) 333 yd (305 m) 333 yd (305 m) 333 yd (305 m) 333 yd (305 m) 333 yd (305 m) 333 yd (305 m) 333 yd (305 m) 333 yd (305 m) 333 yd (305 m) 333 yd (305 m)
2 mil (51 µm)
LFT
834031
VF-HS8171-51-965-305-LFT
ELONGATION
MAX USE TEMP. 400% 400 F / 204 C
2 mil (51 µm)
LFT
834033
VF-HS8171-51-1270-305-LFT
2 mil (51 µm)
LFT
834035
VF-HS8171-51-1575-305-LFT
Available in 2 mil thicknesses up to 3.6 meters wide in standard sheet, v-sheet and lay flat tube formats. * Application is feasible but necessitates validation on a case-by-case basis, primarily considering factors such as temperature and resin type. ** For tube format film (LFT), the width in inches is measured as the envelope’s width, which can be unfolded to double the size.
2 mil (51 µm)
LFT
834037
VF-HS8171-51-1828-305-LFT
2 mil (51 µm)
LTX
834039
VF-HS8171-51-952-305-LTX
2 mil (51 µm)
LTX
834032
VF-HS8171-51-1257-305-LTX 98 in (2490 mm) (open)
2 mil (51 µm)
LTX
834034
VF-HS8171-51-1562-305-LTX 122 in (3100 mm) (open)
2 mil (51 µm)
LTX
834036
VF-HS8171-51-1816-305-LTX 142 in (3600 mm) (open)
36 in (914 mm) 48 in (1219 mm) 60 in (1524 mm) 70 in (1778 mm)
2 mil (51 µm)
SHT
834038
VF-HS8171-51-914-305-SHT
2 mil (51 µm)
SHT
697838
VF-HS8171-51-1219-305-SHT
2 mil (51 µm)
SHT
675664
VF-HS8171-51-1524-305-SHT
2 mil (51 µm)
SHT
834040
VF-HS8171-51-1778-305-SHT
16
Bagging Film
SV4000
SV4000 is a high-elongation nylon-based vacuum bagging film engineered for parts with complex geometries. Its specially formulated nylon composition provides excellent toughness, flexibility, and resistance to tearing, allowing the film to perform reliably in both dry and humid processing environments.
Application: Infusion, oven and autoclave cure cycles Resin: Polyester, Vinyl Ester, Epoxy and Phenolic*
COLOR
TENSILE
PRODUCT CODE
TOTAL THICKNESS
FOLD TYPE
DESCRIPTION
WIDTH
LENGTH
Available in 2 and 3 mil thicknesses up to 4.6 meters wide in standard sheet, v-sheet and lay flat tube formats. *Application is feasible but necessitates validation on a case-by-case basis, primarily considering factors such as temperature and resin type. ** For tube format film (LFT), the width in inches is measured as the envelope’s width, which can be unfolded to double the size. PINK 15,228 PSI ELONGATION MAX USE TEMP. 500% 414 F / 212 C
845586
VFS-SV4000-50-150-200-LFT
6 in (150 mm)**
219 yd (200 m)
2 mil (50 µm)
LFT
845587
VFS-SV4000-50-200-200-LFT
8 in (200 mm)**
219 yd (200 m)
2 mil (50 µm)
LFT
845583
VFS-SV4000-50-300-500-LFT
12 in (300 mm)**
547 yd (500 m)
2 mil (50 µm)
LFT
845582
VFS-SV4000-50-460-305-LFT
18 in (460 mm)**
333 yd (305 m)
2 mil (50 µm)
LFT
838213
VFS-SV4000-50-600-305-LFT
24 in (600 mm)**
333 yd (305 m)
2 mil (50 µm)
LFT
845584
VFS-SV4000-50-690-305-LFT
27 in (690 mm)**
333 yd (305 m)
2 mil (50 µm)
LFT
834241
VFS-SV4000-50-910-305-LFT
36 in (910 mm)**
333 yd (305 m)
2 mil (50 µm)
LFT
834195
VFS-SV4000-50-1220-305-LFT
48 in (1220 mm)**
333 yd (305 m)
2 mil (50 µm)
LFT
834196
VFS-SV4000-50-1370-305-LFT
54 in (1370 mm)**
333 yd (305 m)
2 mil (50 µm)
LFT
834197
VFS-SV4000-50-1520-305-LFT
60 in (1520 mm)**
333 yd (305 m)
2 mil (50 µm)
LFT
834198
VFS-SV4000-50-1830-305-LFT
72 in (1830 mm)**
333 yd (305 m)
2 mil (50 µm)
LFT
834194
VFS-SV4000-75-2300-152-LFT
90 in (2300 mm)**
166 yd (152 m)
3 mil (75 µm)
LFT
834199
VFS-SV4000-50-910-305-LTX
72 in (1830 mm) (open)
333 yd (305 m)
2 mil (50 µm)
LTX
834219
VFS-SV4000-50-1220-305-LTX
96 in (2440 mm) (open)
333 yd (305 m)
2 mil (50 µm)
LTX
834223
VFS-SV4000-50-1370-305-LTX
107 in (2720 mm) (open)
333 yd (305 m)
2 mil (50 µm)
LTX
834212
VFS-SV4000-50-1520-305-LTX
120 in (3050 mm) (open)
333 yd (305 m)
2 mil (50 µm)
LTX
834213
VFS-SV4000-50-1830-305-LTX
144 in (3660 mm) (open)
333 yd (305 m)
2 mil (50 µm)
LTX
834215
VFS-SV4000-75-2300-152-LTX
181 in (4600 mm) (open)
166 yd (152 m)
3 mil (75 µm)
LTX
834225
VFS-SV4000-50-910-610-SHT
36 in (910 mm)
667 yd (610 m)
2 mil (50 µm)
SHT
834214
VFS-SV4000-50-1220-610-SHT
48 in (1220 mm)
667 yd (610 m)
2 mil (50 µm)
SHT
834217
VFS-SV4000-50-1370-305-SHT
54 in (1370 mm)
333 yd (305 m)
2 mil (50 µm)
SHT
834218
VFS-SV4000-50-1520-305-SHT
60 in (1520 mm)
333 yd (305 m)
2 mil (50 µm)
SHT
834220
VFS-SV4000-50-1830-305-SHT
72 in (1830 mm)
333 yd (305 m)
2 mil (50 µm)
SHT
834226
VFS-SV4000-75-2300-152-SHT
91 in (2300 mm)
166 yd (152 m)
3 mil (75 µm)
SHT
17
AEROVAC PRODUCT CATALOG
Bagging Film
HS8171 QUICK DRAW - EMBOSSED
DESCRIPTION HS8171 Quick Draw is fabricated from the same co-extruded modified nylon film as standard HS8171, but with an added embossed textured pattern designed for effective air evacuation during compaction or de-bulking processes. It has undergone qualification according to numerous Aerospace manufacturer specifications. Depending on the geometry and application requirements, this product offers potential cost savings for customers, as it replaces the need for separate bagging film, breather, or release film, streamlining the process into a single item. Application: Compaction or de-bulk Resin of the main application: Polyester, Vinyl Ester, Epoxy, Phenolic and BMI COLOR TENSILE GREEN 14000 PSI ELONGATION MAX USE TEMP. 415% 400 F / 204 C THICKNESS FORMAT WIDTH (INCHES) LENGTH (FEET) 2 mil 2 mil SHT SHT 60 500 500 120
PRODUCT CODE
676352 VF-HS8171QD-51-1524-152-SHT 676349 VF-HS8171QD-51-3048-152-SHT
Available in 2 and 3 mil thicknesses up to 3.048 meters wide in standard sheet format. *Application is feasible but necessitates validation on a case-by-case basis, primarily considering factors such as temperature and resin type.
SV250
SV250 is a polyurethane film known for its exceptional conformability, making it ideal for applications where flexibility and elongation are crucial, particularly in complex geometries. The film is primarily used for debulking purposes, but can also be employed during the curing process, especially in instances of low-temperature processing. Application: Compaction or de-bulk Resin of the main application: Epoxy (cure application), Polyester, Vinyl Ester, Phenolic and BMI
TOTAL THICKNESS
FOLD TYPE
COLOR
TENSILE
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
** Due to its composition as a polyurethane film, it requires the use of a specialized sealing tape, such as VS2042. 11000 PSI ELONGATION MAX USE TEMP. 500% 275 F / 135 C LIGHT BLUE
120 in (3048 mm) (open)
333 yd (305 m) 667 yd (610 m)
676555
VF-SV250-51-1524-305-LTX
2 mil (51 µm)
LTX
676559
VF-SV250-51-1524-610-SHT
60 in (1524 mm)
2 mil (51 µm)
SHT
Available in 1.5 and 2 mil thicknesses up to 3.05 wide without seams & wider widths by heat seaming two larger bags together. *Application is feasible but necessitates validation on a case-by-case basis, primarily considering factors such as temperature and resin type.
500G
500G film is designed for both vacuum bagging and release applications on both sides, suitable for cures up to 302°F. It provides reliable release from most resins used in Aerospace, Automotive, and Marine industries. The embossed version accelerates compaction and debulking, making the process faster and more cost-effective. Additionally, the film can be perforated, as available in the release film portfolio. Application: Compaction or de-bulk Resin of the main application: Polyester, Vinyl Ester, Epoxy, Phenolic and BMI
TOTAL THICKNESS
FOLD TYPE
COLOR GREEN
TENSILE 14000 PSI
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
59 in (1500 mm) 78 in (2000 mm) 98 in (2500 mm)
547 yd (500 m) 547 yd (500 m) 547 yd (500 m)
845122
VFS2-500G-50-1500-500-SHT
2 mil (50 µm)
SHT
ELONGATION
MAX USE TEMP.
845115
VFS2-500G-50-2000-500-SHT
2 mil (50 µm)
SHT
460%
302 F / 150 C
845116
VFS2-500G-50-2500-500-SHT
2 mil (50 µm)
SHT
* Application is feasible but necessitates validation on a case-by-case basis, primarily considering factors such as temperature and resin type.
18
Bagging Film
205B
205B incorporates a polyethylene surface and a polyamide interior, achieving a balance between properties and cost-effectiveness. Additionally, the presence of polyethylene on the surface reduces the influence of humidity on its performance. This film is primarily engineered for the production of large parts and has been shown to work well in low humidity enviroments. Application: Wet lay-up and infusion processes Resin: Polyester, Vinyl Ester and Epoxy
COLOR
TENSILE
TOTAL THICKNESS
FOLD TYPE
PRODUCT CODE
DESCRIPTION
WIDTH
LENGTH
BLUE TD: 650 PSI ELONGATION MAX USE TEMP. 600% 245 F / 120 C
843182
VFS-205B-80-2000-200-SHT
79 in (2000 mm)
219 yd (200 m)
3 mil (80 µm)
SHT
700293
VFS-205B-80-2000-200-LTX
157 in (4000 mm) (open)
219 yd (200 m)
3 mil (80 µm)
LTX
701212
VFS-205B-80-2250-160-GSC 177 in (4500 mm) (open)
175 yd (160 m)
3 mil (80 µm)
GSC
699793
VFS-205B-75-3000-125-GSC 236 in (6000 mm) (open)
137 yd (125 m)
3 mil (75 µm)
GSC
700288
VFS-205B-80-4000-80-GSC
315 in (8000 mm) (open)
87 yd (80 m)
3 mil (80 µm)
GSC
846422
VFS-205B-80-5250-75-GSC 413 in (10500 mm) (open)
82 yd (75 m)
3 mil (80 µm)
GSC
700289
VFS-205B-80-6000-75-GSC 472 in (12000 mm) (open)
82 yd (75 m)
3 mil (80 µm)
GSC
699796
VFS-205B-80-8000-65-GSC 630 in (16000 mm) (open)
71 yd (65 m)
3 mil (80 µm)
GSC
Available in 3 mil thicknesses up to 16 meters wide without seams and wider widths by heat seaming two larger bags together. *Application is feasible but necessitates validation on a case-by-case basis, primarily considering factors such as temperature and resin type.
200G
200G incorporates a multilayered polymer achieving a balance between properties and cost- effectiveness. Additionally, the presence of polyethylene on the surface reduces the influence of humidity on its performance. This film is primarily engineered for the production of large parts. Application: Wet lay-up and infusion processes Resin: Polyester, Vinyl Ester and Epoxy
PRODUCT CODE
TOTAL THICKNESS
FOLD TYPE
DESCRIPTION
WIDTH
LENGTH
COLOR
TENSILE
832016 831768 832610
VF-200G-75-2000-150-LTX 157 in (4000 mm) (open) VFS-200G-80-3000-125-CSC 236 in (6000 mm) (open) VFS-200G-80-4000-80-GSC 315 in (8000 mm) (open)
164 yd (150 m) 3 mil (75 µm) 137 yd (125 m) 3 mil (80 µm)
LTX
GREEN TD: 6500 PSI ELONGATION MAX USE TEMP. 500% 245 F / 120 C
CSC GSC
87 yd (80 m)
3 mil (80 µm)
690309
VFS-200G-80-5000-75-GSC 393 in (10000 mm) (open)
82 yd (75 m)
3 mil (80 µm)
GSC
695112 676238
VFS-200G-80-6000-75-GSC 472 in (12000 mm) (open) VF-200G-75-8000-40-GSC 630 in (16000 mm) (open)
82 yd (75 m) 44 yd (40 m)
3 mil (80 µm) 3 mil (75 µm)
GSC GSC
Available in 3 mil thicknesses up to 16 meters wide without seams and wider widths by heat seaming two larger bags together. Film with a width of up to 8 meters has lower prices. *Application is feasible but necessitates validation on a case-by-case basis, primarily considering factors such as temperature and resin type.
19
AEROVAC PRODUCT CATALOG
Bagging Film
UHT 750
UHT 750 is a high-performance polyimide vacuum bagging film developed for demanding Aerospace composite applications. It is designed for high-temperature autoclave and oven cure cycles, maintaining dimensional stability and mechanical integrity throughout the cure process. Application: Autoclave and oven cure cycles Resin: Epoxy, Phenolic, BMI and high-temperature thermoplastic systems
COLOR AMBER
TENSILE 39160 PSI
PRODUCT CODE
DESCRIPTION
THICKNESS
WIDTH
LENGTH FOLDER
0.002 in (51 µm) 0.002 in (51 µm)
60 in (1524 mm) 48 in (1219 mm)
341 ft (104 m) 341 ft (104 m)
232201
VF-UHT750-51-1524-104-SHT
SHT
MATERIAL POLYIMIDE
MAX USE TEMP.
800 F / 426 C
844665
VF-UHT750-51-1219-104-SHT
SHT
450V
450V is a tough yet flexible co-extruded vacuum bagging film designed for demanding composite processing applications. Suitable for infusion, oven, and autoclave processes, it offers excellent drapeability, durability, and vacuum integrity under pressure. Designed for temperatures up to 338°F (170°C), 450V performs well across Aerospace, Wind Energy, and industrial composite applications. Application: Infusion, Oven and Autoclave Resin: Epoxy, Polyester, Vinyl Ester and Phenolic
COLOR PURPLE
TENSILE 6092 PSI
PRODUCT CODE
DESCRIPTION
THICKNESS
WIDTH
LENGTH FOLDER
3 mil (75 µm) 2 mil (50 µm) 3 mil (75 µm) 3 mil (75 µm) 2 mil (50 µm) 5 mil (125 µm)
59 in (1500 mm) 35 in (900 mm) 72 in (1830 mm) 84 in (2134 mm) 79 in (2000 mm) 54 in (1370 mm)
240 yd (220 m) 167 yd (153 m) 167 yd (153 m) 666 yd (609 m) 427 yd (390 m) 1203 yd (1100 m)
680859
VFS-450V(HS)-75-1500-220-SHT
SHT
ELONGATION
MAX USE TEMP.
400%
338 F / 170 C
698279
VFS-450V(HS)-50-900-305-LFT
LFT
687243
VFS-450V(HS)-75-1830-153-LFT
LFT
852019
VFS-450V(HS)-75-2134-609-SHT
SHT
698277
VFS-450V(HS)-50-2000-390-SHT
SHT
698814 VFS-450V(HS)-125-1370-1100-SHT
SHT